Fumasep F-10150-PF

Brand: FuMA-Tech
Product Code: 5041629

Qty: - +
   - OR -   

Please note that this material has been discontinued. Limited stock remains.

Fumasep F-10150-PF is a Perfluorinated PFA reinforced Cation Exchange Membrane (CEM) with low resistance, high mechanical stability, high selectivity and high chemical / oxidative stability, and resistant to chlorine.

Fumasep F-10150-PF membrane comes in a 20cm x 30cm size sheet. The membrane is the colourless, transparent foil, delivered on a backing layer (colourless rigid PET foil). Peel off carefully the membrane from the backing layer.

Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.

Fumasep F-10150-PF Features:
 

 • Applications: Electrochemical processes requiring cation exchange membranes with high oxidative stability and highly resistant to chlorine (e.g. for electrolysis, for electrode protection in electrodialysis, and others).
 • Cation Exchange Membrane (CEM)
 • Thickness: 140 - 150 micrometers (5.51 - 5.91 mil)
 • Size: 20cm x 30cm

Fumasep F-10150-PF Technical Specification Sheet

Handling:

Keep membrane package closed / sealed when unused. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections. Membranes will expand and contract based on water / electrolyte content.

Pre-Treatment and Conditioning:

The membrane is delivered in H-form and dry form (non-activated). In many applications no further pretreatment is required. However, for optimum performance and lowest resistance it is recommended to pretreat the membrane according to the following prescription: Put the membrane sample in an aqueous 10 wt% HNO3 solution or in 5 vol % H2SO4 solution at minimum 80°C for at least 12 hours. After rinsing with demineralized water (pH ~ 7) the membrane is ready for use (activated). Membranes will expand and contract based on moisture content.

If you have any concerns about storage, chemical stability, pre-treatment or before proceeding, please feel free to contact us for further information.

Long Term Storage:

The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use.

Please note that a current lead time of one to two weeks is to be expected.

Membrane Properties
Membrane Cation Exchange Membrane
Thickness 140 - 150 µm (microns)
Appearance / Color Transparent / Colorless
Backing Foil PET Foil
Delivery Form Dry (non-activated)
Reinforcement PFA
Counter Ion H-form
Density 25 - 30 mg•cm-2
Specific Area Resistance 1.8 - 2.9 (Na+ form) Ω•cm2
Specific Conductivity 6 - 9 (Na+ form) mS•cm-1
Selectivity 94 - 98 %
Hydroxyl Transfer Rate 250 - 400 µmol•min-1•cm-2
Ion Exchange Capacity 0.7 - 0.9 meq•g-1
Dimensional Swelling in H2O at 25°C 8 - 12 (in H-form) %
Uptake in H2O at 25°C 15 - 25 (in H-form) wt %
Non-Std Modulus (MPa) 400 - 700 MPa
Tensile Strength - max. (MPa) 15 - 20 MPa
Elongation to Break (%) 20 - 50 %
pH Stability Range at 25°C 0 - 14 pH
Bubble Point Test in Water at 25°C > 3 bar