Fumapem F-1030

Product Code: 5041730

Price:
From $18.00

Available Options


* Size (cm):

Qty: - +
   - OR -   

Fumapem F‐1030 membrane is a perfluorinated cation-exchange membrane with low resistance, high mechanical stability, low dimensional swelling, and high stability in acidic environment. The polymer composition of this membrane is based on the perflurosulfonic acid resin with long side chains.

Fumapem F‐1030 membrane comes in either a 10cm x 10cm or 20cm x 30cm size sheet.

Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.

Fumapem F‐1030 Features:
 

• Applications: Redox-Flow Battery, e.g. Vanadium-Redox-Flow Battery (VRB), using aqueous acidic conditions
• Cation Exchange Membrane
• Thickness: 30 micrometers (1.18 mil)
• Sizes: 10cm x 10cm, 20cm x 30cm

 Fumapem F‐1030 Technical Specification Sheet

Delivery:

The membrane is the transparent (slightly opaque) foil, delivered on a backing foil (colourless rigid PET foil). Pull off carefully the membrane from the backing foil. The membrane is ready to use.

Handling:

Keep membrane package closed / sealed when unused. Unpack membrane only for direct use and process immediately after opening. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.

Pre-Treatment and Conditioning:

The membrane is delivered in H-form and dry form. The membrane does not need any pretreatment and is ready for use. Please assemble the membrane in dry form.

Long Term Storage:

The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use.

Please note that a current lead time of one to two weeks is to be expected.

Membrane Properties
Backing Foil PET Foil
Delivery Form Dry
Reinforcement None
Tensile Strength - max. (MPa) 35 - 46 MPa
Elongation to Break (%) 80 - 150 %
Counter Ion H+ Form
Selectivity > 98 %
Proton Transfer Rate > 7000 µmol•min-1•cm-2
Bubble Point Test in Water at 25°C > 3 bar
Plate Physical Properties
Young's Modulus - Dynamic 260 - 300 MPa