Fumapem F-930-RFS

Brand: FuMA-Tech
Product Code: 5041652

Qty: - +

- OR -

Fumapem F-930-RFS membrane is a perflourinated cation exchange membrane with low resistance, high mechanical stability, low dimensional swelling, and high stability in acidic environments. The perfluorinated sulfonic acid (PFSA) membrane's functional sites are based on long side chain (LSC) composition.

Fumapem F-930-RFS membrane comes in either a 10cm x 10cm or 20cm x 30cm size sheet.

Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.

Fumapem F-930-RFS Features:

• Applications: Designed for Fuel Cell Application (H2-PEMFC)
• Cation Exchange Membrane
• Thickness: 28 - 33 micrometers (1.11 - 1.29 mil)
• Sizes: 10cm x 10cm, 20cm x 30cm

Fumapem F-930-RFS Technical Specification Sheet

Delivery:

The membrane is the transparent foil, delivered on a backing layer (colorless rigid PET foil). Peel off carefully the membrane from the backing layer. The membrane is ready for use.

Handling:

Keep membrane package closed / sealed when unused. Unpack membrane only for direct use and process immediately after opening. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.

Pre-Treatment and Conditioning:

The membrane does not need any pre-treatment and is ready for use. Please assemble the membrane in dry form. If you have any concerns about storage, chemical stability, and pre-treatment please feel free to contact us for further information.

Long Term Storage:

The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use.

Please note that a current lead time of one to two weeks is to be expected.

Membrane Properties
Membrane	Cation Exchange Membrane
Thickness	28 - 33 µm (microns)
Appearance / Color	Transparent / Colorless
Backing Foil	PET Foil
Delivery Form	Dry
Reinforcement	Yes
Tensile Strength - max. (MPa)	> 20 MPa
Non-Std Modulus (MPa)	> 230 MPa
Yield Strength at 23°C / 50 % R.H.	> 10 MPa
Elongation to Break (%)	> 150 %
Specific Area Resistance	< 0.15 (in H2O at 25°C in H-form) Ω•cm2
Specific Conductivity	110 (in H2O at 25°C in H-form) mS•cm-1
Counter Ion	H-form
Ion Exchange Capacity	0.89 - 1.02 (in H2O at 25°C in H-form) meq•g-1
Uptake in H2O at 25°C	15 (in H-form) wt %
Dimensional Swelling in H2O at 25°C	3 (in H-form) %