- Fuel Cell Cars
- Fuel Cell Stacks
Fuel Cell Testing
- - Fixed Testing Systems
- - Liquid and Gas Delivery Systems
- - Fuel Cell Testing Hardware
- - Modular Testing Systems
- - Vacuum Tables and Temperature Controllers
- - Electronic Measurement and Control
- - Stack Humidification Systems
- - Ion Exchange Filters
- - Fuel Cell Testing Components
- - Portable Generators
- - Electrochemical Experiments
- Fuel Cell Components
- Hydrogen Equipment
- Power Devices
- Solar Power
- Hydro Power
- Wind Power
- Bioenergy Power
- Lab Accessories
- STEM Education
Fumapem F-950 membrane is a Long Side Chain - Per-Fluorinated Sulfonic Acid (LSC-PFSA) cation exchange membrane (CEM) with low resistance, high mechanical stability, high selectivity and high chemical / oxidative stability.
Fumapem F-950 is a thin longside-chain non-reinforced membrane that is designed for use in stationary hydrogen PEM fuel cell applications.
• Applications: Designed for Stationary Proton Exchange Membrane Fuel Cell applications.
• Cation Exchange Membrane
• Equivalent Weight of 950 (g/eq)
• Long Side Chain - Per-Fluorinated Sulfonic Acid (LSC-PFSA)
• Thickness: 50 micrometers (1.97 mil)
• Size: 20cm x 30cm or 10 cm x 10cm
The membrane is the colorless, transparent foil, delivered on a backing layer (colourless rigid PET foil). Pull off carefully the membrane from the backing foil. Before use the membrane must be activated.
Keep membrane package closed / sealed when unused. Unpack membrane only for direct use and process immediately after opening. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.
Membranes will expand and contract based on water / electrolyte content. To eliminate wrinkling, it is necessary to expand membranes before mounting by pretreatment.
The membrane is delivered in H-form and dry form (non-activated). For optimum performance and lowest resistance it is necessary to pretreat the membrane according to the following prescription: Put the membrane sample in an aqueous 10 wt% HNO3 solution or in 5 vol % H2SO4 solution at minimum 80°C for at least 12 hours. After rinsing with demineralized water (pH ~ 7) the membrane is ready for use (activated). Membranes will expand and contract based on moisture content.
Please note that this product has been discontinued, and a limited supply is available.
|Membrane||Cation Exchange Membrane|
|Thickness||44 - 49 µm (microns)|
|Appearance / Color||Transparent|
|Backing Foil||PET Foil|
|Tensile Strength - max. (MPa)||30 - 35 MPa|
|Non-Std Modulus (MPa)||500 - 550 MPa|
|Elongation to Break (%)||125 - 160 %|
|Selectivity||93 - 94 % (0.1 / 0.5 mol/kg KCl at T = 25 °C)|
|Dimensional Swelling in H2O at 25°C||12 - 14 % ( 2 M H2SO4 at T = 25 °C)|
|Proton Transfer Rate||> 10,000 µmol•min-1•cm-2|
|Bubble Point Test in Water at 25°C||> 3 bar|