- Fuel Cell Cars
- Fuel Cell Stacks
Fuel Cell Testing
- - Fixed Testing Systems
- - Liquid and Gas Delivery Systems
- - Fuel Cell Testing Hardware
- - Modular Testing Systems
- - Vacuum Tables and Temperature Controllers
- - Pressure Monitoring
- - Electronic Measurement and Control
- - Stack Humidification Systems
- - Ion Exchange Filters
- - Fuel Cell Testing Components
- Fuel Cell Components
- Hydrogen Equipment
- Laboratory Gas Generators
- Power Devices
- Solar Power
- Hydro Power
- Wind Power
- Bioenergy Power
- Lab Accessories
- STEM Education
Fumasep FAB-PPS-130 is an anion-exchange membrane - PPS-reinforced with high proton blocking capability, high selectivity, very high mechanical stability, and high stability in acidic and caustic environment.
Fumasep FAB-PPS-130 membrane comes in either a 10cm x 10cm or 20cm x 30cm size sheet.
Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.
• Applications: Electrodialysis and electrodialysis with bipolar membranes
• Anion Exchange Membrane
• Thickness (dry): 105 - 140 micrometers (4.13 - 5.51 mil)
• Sizes: 10cm x 10cm, 20cm x 30cm
The membrane is the brown foil delivered in dry form.
Keep membrane package closed / sealed when unused. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.
Wet form: Storage for short and medium time scale (hours up to several weeks) may be done in unsealed containers in 0.5 - 1.5 wt% NaCl solution or comparable neutral pH electrolytes. For storage over a longer time period a sealed container is recommended using afore said electrolyte with biocide to avoid biological fouling.
The membrane is delivered in bromide form and dry form. If additional cleaning is required rinse the membrane either in the application solution or a NaCl solution according to the application requirement. Do not let the membrane dry out since micro-cracks may likely occur during drying. If you have any concerns about storage, chemical stability, pre-treatment or before proceeding, please feel free to contact us for further information.
Please note that a current lead time of one to two weeks is to be expected.
|Membrane||Anion Exchange Membrane|
|Thickness||105 - 140 µm (microns)|
|Appearance / Color||Brown, transparent|
|Tensile Strength - max. (MPa)||> 60 MPa|
|Yield Strength at 23°C / 50 % R.H.||> 45 MPa|
|Ion Exchange Capacity||0.9 - 1.15 meq•g-1|
|Selectivity||> 93 %|
|Dimensional Swelling in H2O at 25°C||< 2 %|
|Proton Transfer Rate||< 300 µmol min^-1 cm^-2|
|Bubble Point Test in Water at 25°C||> 3 bar|