- Fuel Cell Cars
- Fuel Cell Stacks
Fuel Cell Testing
- - Fixed Testing Systems
- - Liquid and Gas Delivery Systems
- - Fuel Cell Testing Hardware
- - Modular Testing Systems
- - Vacuum Tables and Temperature Controllers
- - Electronic Measurement and Control
- - Stack Humidification Systems
- - Ion Exchange Filters
- - Fuel Cell Testing Components
- - Portable Generators
- - Electrochemical Experiments
- Fuel Cell Components
- Hydrogen Equipment
- Power Devices
- Solar Power
- Hydro Power
- Wind Power
- Bioenergy Power
- Lab Accessories
- STEM Education
Please be aware that this product has been discontinued. We have a very limited amount remaining in stock.
Fumasep FKM-PP is a heterogeneous cation-exchange membrane - PP-reinforced with high selectivity and very high mechanical stability. The polymer backbone for this cation exchange membrane is based on a hydrocarbon polymer material.
Fumasep FKM-PP membrane comes in either a 10cm x 10cm or 20cm x 30cm size sheet.
Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.
• Applications: Electrocoating, electroplating, electrodeionisation, electrodialysis for demineralisation, desalination
• Cation Exchange Membrane
• Stability Range: pH 1 - 10 at T = 25 °C
• Thickness (dry): 450 - 500 micrometers (17.71 - 19.69 mil)
• Sizes: 10cm x 10cm, 20cm x 30cm
The membrane is the brown foil delivered in dry form.
Keep membrane package closed / sealed when unused. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.
Dry form: Storage for long time scale (> 12 month) may be done in dry state (sealed container). Wet form: Storage for short and medium time scale (hours up to several weeks) may be done in unsealed containers in 0.5 – 1.5 wt% NaCl solution or comparable neutral pH electrolytes. For storage over a longer time period a sealed container is recommended using afore said electrolyte with biocide to avoid biological fouling.
The membrane is delivered in Na form and dry form. Depending on application and cell design, assembling is possible in dry form (without pretreatment) or wet form. For optimum performance it is recommended to rinse the membrane in NaCl solution (e.g. 0.5 M NaCl solution at T = 25 °C for 24 hrs) to remove any additive from the membrane. Do not let the membrane dry out since micro-cracks may likely occur during shrinkage.
The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use.
|Membrane||Cation Exchange Membrane|
|Thickness||450 - 500 µm (microns)|
|Appearance / Color||Brown|
|Reinforcement||PP (polypropylene fabrics)|
|Specific Conductivity||1.7 - 2.0 mS•cm-1|
|Ion Exchange Capacity||1.6 meq•g-1|
|Selectivity||93 - 96 %|
|Uptake in H2O at 25°C||15 - 20 wt%|
|Weight Per Unit Area||44 - 52 mg cm2|
|Dimensional Swelling in H2O at 25°C||0 - 2 %|
|Hydroxyl Transfer Rate||50 μmol•min-1•cm-2|
|Bubble Point Test in Water at 25°C||> 3 bar|
|pH Stability Range at 25°C||1 - 10 pH|