Fumasep FKL-PK-130

Brand: FuMA-Tech
Product Code: 34010009

Price:
From $31.00

Available Options


* Size (cm):

Qty: - +
   - OR -   

Fumasep FKL-PK-130 is a PK reinforced Cation Exchange Membrane (CEM) with high hydroxyl blocking capability, high selectivity, high mechanical stability, and high stability in acidic and caustic environment. The polymer backbone for this membrane is based on a proprietary hydrocarbon resin.

Fumasep FKL-PK-130 membrane comes in either a 10cm x 10cm or 20cm x 30cm size sheet.

Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.

Fumasep FKL-PK-130 Features:
 

 • Applications: Process for concentrating alkaline solutions, electrodialysis and electrodialysis with bipolar membranes.
 • Cation Exchange Membrane
 • Stability Rang (pH) at 25°C: Stable under acidic and caustic conditions.
 • Thickness: 130 micrometers (5.1 mil)
 • Sizes: 10cm x 10cm, 20cm x 30cm

Fumasep FKL-PK-130 Technical Specification Sheet

Handling:

Keep membrane package closed / sealed when unused. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.

Storage:

Dry Form: The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use.

Wet Form: Storage for short and medium time scale (hours up to several weeks) may be done in unsealed containers in 0.5 - 1.5 wt% NaCl solution or comparable neutral pH electrolytes.  For storage over a longer time period a sealed container is recommended using afore said electrolyte with ca. 100 ppm biocide (NaN3) to avoid biological fouling.

Pre-Treatment and Conditioning:

The membrane is delivered in H-form and dry form. Depending on application and cell design, assembling is possible in dry form (without pretreatment) or wet form. For optimum performance it is recommended to rinse the membrane in NaCl solution (e.g. 0.5 M NaCl solution at 25°C for 24 hrs) to remove any additive from the membrane. Place the membrane sample between stabilizing meshes / spacers in order to avoid curling. Do not let the membrane dry out since micro-cracks may likely occur during shrinkage.

If you have any concerns about storage, chemical stability and pretreatment before proceeding, please feel free to contact us for further information.

Please note that a current lead time of one to two weeks is to be expected.

Membrane Properties
Membrane Cation Exchange Membrane
Thickness 110 - 140 µm (microns)
Appearance / Color Brown
Backing Foil None
Delivery Form Dry
Reinforcement PK
Counter Ion Protonic form (H+)
Density 10 - 13 mg•cm-2
Specific Area Resistance 3 - 10 (in Na+ form) Ω•cm2
Specific Conductivity 1 - 4 (in Na+ form) mS•cm-1
Selectivity 96 - 99 %
Hydroxyl Transfer Rate 5 - 50 µmol•min-1•cm-2
Ion Exchange Capacity 0.6 - 0.8 (in Na+ form) meq•g-1
Dimensional Swelling in H2O at 25°C 0 - 2 %
Uptake in H2O at 25°C 10 - 25 wt %
Non-Std Modulus (MPa) 1000 - 2000 MPa
Tensile Strength - max. (MPa) 50 - 80 MPa
Yield Strength at 23°C / 50 % R.H. 20 - 30 MPa
Elongation to Break (%) 20 - 50 %
Bubble Point Test in Water at 25°C > 3 bar