Your shopping cart is empty!
+1 (855) 251-0016 | sales@fuelcellstore.com
Categories
- Fuel Cell Cars
- Education
- Fuel Cell Stacks
-
Fuel Cell Testing
- - Fixed Testing Systems
- - Liquid and Gas Delivery Systems
- - Fuel Cell Testing Hardware
- - Modular Testing Systems
- - Vacuum Tables and Temperature Controllers
- - Electronic Measurement and Control
- - Stack Humidification Systems
- - Ion Exchange Filters
- - Fuel Cell Testing Components
- - Portable Generators
- - Electrochemical Experiments
- Fuel Cell Components
- Hydrogen Equipment
- Power Devices
- Solar Power
- Hydro Power
- Wind Power
- Bioenergy Power
- Lab Accessories
- Clearance
- STEM Education
- Summer Sale
Nafion™ 115
Price:
From $28.00
Nafion™ Membrane is used to separate the anode and cathode compartment of Proton Exchange Membrane fuel cells and water electrolyzers. The thickness of this particular cation exchange membrane, Nafion™ 115 makes it suitable for Direct Methanol Fuel Cells (DMFC) and Electrolysis applications. Nafion™ 115 is 127 micrometers (5 mil) thick.
Chemours (formerly DuPont) Nafion™ 115 membranes are non-reinforced films based on chemically stabilized perfluorosulfonic acid/PTFE copolymer in the acid (H+) form. The physical properties remain the same for the chemically stabilized membranes, which exhibit substantially lower fluoride ion release compared to the non-stabilized polymer – a sign of improved chemical durability. Nafion™ PFSA membranes are widely used for Proton Exchange Membrane (PEM) fuel cells and water electrolyzers. The membrane performs as a separator and solid electrolyte in a variety of electrochemical cells that require the membrane to selectively transport cations across the cell junction. The polymer is chemically resistant and durable.
Please contact us at sales@fuelcellstore.com for the SDS and technical data sheets (TDS).
| Membrane Properties | |
| Thickness | 127 micrometers (5 mil) |
| Basic Weight (g/m²) | 250 |
| Tensile Strength - max. (MPa) | 43 (6.2) in MD, 32 (4.6) in TD - Method: ASTM D 882 |
| Non-Std Modulus (MPa) | 249 (36) - Method: ASTM D 882 |
| Elongation to Break (%) | 225 (MD), 310 (TD) - Method: ASTM D 882 |
| Tear Resistance - Initial (g/mm) | 6000 (MD, TD) - Method: ASTM D 1004 |
| Tear Resistance - Propagating (g/mm) | >100 (MD), >150 (TD) - Method: ASTM D 1922 |
| Specific Gravity (23 °C, 50% RH) | 1.98 |
| Available Acid Capacity (meq/g) | 0.90 min |
| Total Acid Capacity (meq/g) | 0.95 to 1.01 |
| Conductivity (S/cm) | 0.10 min |
| Membrane Hydrolytic Properties | |
| Water content (% water) | 5.0 - Method: ASTM D 570 |
| Water uptake (% water) | 38.0 - Method: ASTM D 570 |
| Linear Expansion % increase - 50% RH, 23°C to water soaked 23°C | 10.0 - Method: ASTM D 756 |
| Linear Expansion % increase - 50% RH, 23°C to water soaked 100°C | 15.0 - Method: ASTM D 756 |