Nafion™ NE1035

Brand: Chemours
Product Code: 593264

Qty: - +
   - OR -   

Please note that NE1035 has been discontinued by Chemours and only limited supplies are available for the time being.

Nafion™ Membrane NE1035 is used to separate the anode and cathode compartment of Proton Exchange Membrane fuel cells, batteries and water electrolyzers. Nafiion 1035 has a low Equivalent Weight (1000EW) and a higher conductivity, making it particularly suitable for energy storage applications, such as batteries, Direct Methanol Fuel Cells (DMFC) and Electrolysis applications. Nafion™ NE1035 is a 89 micrometer (3.5 mil) thick cation exchange membrane.

Chemours Nafion™ NE1035, EW1000 membranes are non-reinforced films based on chemically stabilized perfluorosulfonic acid/PTFE copolymer in the acid (H+) form. The physical properties remain the same for the chemically stabilized membranes, which exhibit substantially lower fluoride ion release compared to the non-stabilized polymer – a sign of improved chemical durability. Nafion™ PFSA membranes are widely used for Proton Exchange Membrane (PEM) fuel cells and water electrolyzers. The membrane performs as a separator and solid electrolyte in a variety of electrochemical cells that require the membrane to selectively transport cations across the cell junction. The polymer is chemically resistant and durable.

Nafion™ NE1035 Technical Information

Handling and Storage of DuPont Nafion™ Perfluorinated Membranes

Nafion™ Membrane Technical Bulletin No. 93-01 for "DRY" H+ Membrane Pretreatment

Nafion™ Membrane Safety Handling Technical Information Bulletin T-01

Membrane Properties
Thickness 89 micrometer (3.5 mil)
Tensile Strength - max. (MPa) 38 Mpa at 10% RH, 23°C and 19 Mpa at 369 Mpa at water soaked, 23°C
Non-Std Modulus (MPa) 369 Mpa at 10% RH, 23°C and 90 Mpa at 369 Mpa at water soaked, 23°C
Elongation to Break (%) 148% at 10% RH, 23°C and 133% Mpa at 369 Mpa at water soaked, 23°C
Specific Gravity (23 °C, 50% RH) 2
Available Acid Capacity (meq/g) 1.0 min
Total Acid Capacity (meq/g) 1.03 to 1.12
Conductivity (S/cm) 0.106
Membrane Hydrolytic Properties
Water content (% water) ~5%
Water uptake (% water) 43%