ePTFE Reinforced PFSA Membrane (80 microns thick) for PEM Electrolyzers is used to separate the anode and cathode compartment of PEM electrolyzer stacks that usually consume electricity and DI-water in order to generate hydrogen and oxygen gases and requires achieving high current densities (which necessitates the use of a relatively thin membrane, yet mechanically robust enough for PEM electrolyzer applications). PEM electrolyzer industry has recently been moving in the direction of using mechanically reinforced proton exchange membranes in order to provide very robust and reliable electrolyzer stacks. This mechanically reinforced PFSA membrane has a thickness of ~80 microns and ideally suited for PEM electrolyzer stacks that would yield very high current densities and long operational lifetimes. The mechanical reinforcement in this membrane is based on the microporous ePTFE which has 3-D porous regions where the ionically conducting PFSA is wet impregnated via solution cast method. Considering ePTFE Reinforced PFSA Membrane (80 microns thick) for PEM Electrolyzers will broaden researchers horizon by providing an equally valuable avenue to explore, alongside Nafion N115 and Nafion N117 membranes (which are unreinforced membranes) and several other ePTFE reinforced membranes from other vendors.
The major benefit of mechanically reinforced PFSA membranes would be their significantly enhanced operational lifetime compared to the unreinforced PFSA membranes due to swelling related stresses being taken up by the ePTFE reinforcement. One of the major limitations of the mechanically reinforced PFSA membranes is their lower proton or ionic conductivity compared to unreinforced membranes because of less ionically conducting material per unit volume or per unit mass (while ePTFE reinforcement is quite porous, it does have a mass regardless). While it is not a common practice, this membrane product can also be used in PEM fuel cells (especially H2/O2 reactants consuming PEM fuel cells), electrochemical sensors and other relevant technologies that would have a need for thin and mechanically reinforced proton exchange membrane for its operation.
ePTFE Reinforced PFSA Membrane (80 microns thick) for PEM Electrolyzers is based on the chemically stabilized perfluorosulfonic acid material and it is shipped in the acid (H+) form (which is also known as protonic form). Chemical stabilization is also known as end-group stabilization where the carbon atoms that end of the PFSA polymer chains are fully fluorinated. Chemically stabilized PFSA membranes will exhibit substantially lower fluoride ion release compared to the PFSA membranes manufactured from unstabilized PFSA resin. Functional groups (also known as sulfonic acid sites) for this PFSA membrane are based on the long side chain for its chemical structure.
Proton exchange membranes are also known as cation exchange membranes in the market. This PFSA membrane performs as a separator and solid electrolyte (without the need of a liquid acid) in a variety of electrochemical cells that require the membrane to selectively transport protons or other various cations across the cell junction (or between anode and cathode catalyst layers). The polymer is chemically resistant and durable.
Please contact us at firstname.lastname@example.org for the SDS and technical data sheets (TDS).
|80±3 micrometers (per GB/T20043.2022)
|> 0.050 S/cm (or ≥ 50 mS/cm)
|> 250 / 250 MPa (MD/TD) (per GB/T20043.2022)
|Tensile Strength - max. (MPa)
|> 35 / 35 MPa (MD/TD) (per GB/T20043.2022)
|Elongation to Break (%)
|> 100% / 100% (MD/TD) (per GB/T20043.2022)
|Membrane Hydrolytic Properties
|Water content (% water)
|>20/20 (MD/TD) (per GB/T20043.2022)
|<5%, <5% (MD/TD) (per GB/T20043.2022)