- Fuel Cell Cars
- Fuel Cell Stacks
Fuel Cell Testing
- - Fixed Testing Systems
- - Liquid and Gas Delivery Systems
- - Fuel Cell Testing Hardware
- - Modular Testing Systems
- - Vacuum Tables and Temperature Controllers
- - Electronic Measurement and Control
- - Stack Humidification Systems
- - Ion Exchange Filters
- - Fuel Cell Testing Components
- - Portable Generators
- - Electrochemical Experiments
- Fuel Cell Components
- Hydrogen Equipment
- Power Devices
- Solar Power
- Hydro Power
- Wind Power
- Bioenergy Power
- Lab Accessories
- STEM Education
Fumasep F-10120-PK is a PK reinforced Cation Exchange Membrane (CEM) with low resistance, high mechanical stability, high selectivity and high chemical / oxidative stability, and resistant to chlorine.
Fumasep F-10120-PK membrane comes in a 20cm x 30cm size sheet. The membrane is the colourless, transparent foil, delivered on a backing layer (colourless rigid PET foil). Peel off carefully the membrane from the backing layer.
Fumatech membranes are highly sensitive to differences in humidity and moisture content. Therefore the membranes can vary +/- 0.5cm from the original cut sizes. Also due to this sensitivity the manufacturer expects wrinkles to form, however soaking the membranes in deionized water will return the membranes to the full size planar state according to the manufacturer.
• Applications: Electrochemical processes requiring cation exchange membranes with high oxidative stability and highly resistant to chlorine (e.g. for electrode protection).
• Cation Exchange Membrane (CEM)
• Thickness: 120 micrometers (4.72 mil)
• Size: 20cm x 30cm
Keep membrane package closed / sealed when unused. Store, handle and process the membrane in a clean and dust-free area. Use only new and sharp knives or blades, when cutting the membrane. Always wear protective gloves when handling the membrane. Handle with care, be sure not to puncture, crease or scratch the membrane, otherwise leaks will occur. All surfaces in contact with the membrane during handling, inspection, storage and mounting must be smooth and free of sharp projections.
Membranes will expand and contract based on water / electrolyte content.
The membrane is delivered in H-form and dry form (non-activated). For optimum performance and lowest resistance it is necessary to pretreat the membrane according to the following prescription: Put the membrane sample in an aqueous 10 wt% HNO3 solution or in 5 vol % H2SO4 solution at minimum 80°C for at least 12 hours. After rinsing with demineralized water (pH ~ 7) the membrane is ready for use (activated). Membranes will expand and contract based on moisture content.
If you have any concerns about storage, chemical stability, pre-treatment or before proceeding, please feel free to contact us for further information.
The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use.
Please note that a current lead time of one to two weeks is to be expected.
|Membrane||Cation Exchange Membrane|
|Thickness||120 - 135 µm (microns)|
|Appearance / Color||Transparent / Colorless|
|Backing Foil||PET Foil|
|Delivery Form||Dry (non-activated)|
|Tensile Strength - max. (MPa)||35 - 36 MPa|
|Non-Std Modulus (MPa)||660 - 830 MPa|
|Elongation to Break (%)||38 - 42 %|
|Specific Area Resistance||0.33 in 0.5 M H2SO4 and 0.98 in 0.5 M H2SO4 + 0.4 M VOSO4 Ω•cm2|
|Specific Conductivity||54.4 in 0.5 M H2SO4 and 18.1 in 0.5 M H2SO4 + 0.4 M VOSO4 mS•cm-1|
|Ion Exchange Capacity||0.79 meq•g-1|
|Uptake in H2O at 25°C||13 in 2M H2SO4 and 10 in vanadyl sulfate wt %|
|Dimensional Swelling in H2O at 25°C||4 in 2M H2SO4 and 2 in vanadyl sulfate %|
|Bubble Point Test in Water at 25°C||> 3 bar|